FIELD: medicine.SUBSTANCE: calcined alloy for ceramic-faced restoration contains, %: nickel - 37 or more； chromium 18-23.5； molybdenum and/or tungsten - 8-16 in all； (i) silicone - 0.5-3.4 and boron 0.31-2.5, or (ii) silicone 2.1-3.4 and boron 0-0.05； niobium 0.1-0.8； manganese 0.1-0.5； carbon 0-0.02； iron, cobalt, copper - 0-30 in all； aluminium, titanium, zirconium, hafnium, yttrium, lanthanum, cerium, other rare-earth metals, calcium, strontium - 0-0.5 in all； beryllium 0-0.3； and vanadium, tantalum and nitrogen - max. 0.1 in all. The presented weight percentages are always specified at total weight of the alloy. What is also presented is ceramic-faced restoration comprising a denture frame made of said alloy, and dental ceramics calcined on the denture frame and having a thermal-expansion coefficient (TEC) falling within the range of 12 to 14·10-6 K-1 (25-500°C).EFFECT: alloy composition provides a range of useful properties which can be ensured without the use of toxic and cancer-inducing beryllium, low fusion range, unique and easy recognition of the casting moment, high-precision seating of the cast frames, acceptable hardness, applicability of laser welding, high casting characteristics of the alloy； the alloy may be faced by all known facing materials, favourable chemical adhesion of ceramic facing, no calcining deformation ensured by high thermal stability.17 cl, 1 tbl, 13 exГруппа изобретений относится к области стоматологии и касается сплавов для получения облицованной керамикой реставрации зуба. Пригодный для обжига сплав для получения облицованной керамикой реставрации зубов содержит в мас.%: никель - 37 или более； хром 18-23,5； молибден и/или вольфрам - всего 8-16； (i) кремний 0,5-3,4 и бор 0,31-2,5, либо (ii) кремний 2,1-3,4 и бор 0-0,05； ниобий 0,1-0,8； марганец 0,1-0,5； углерод 0-0,02； железо, кобальт, медь - всего 0-30； алюминий, титан, цирконий, гафний, иттрий, лантан, церий, прочие редкоземельные металлы, кальций, стронций - всего 0-0,5； берил