The present invention provides a photopolymerizable composition comprising 50 to 90% by weight of at least one urethane component, 5 to 50% by weight of at least one reactive diluent, 0.1 to 5% by weight of a photoinitiator, and optionally an inhibitor, The composition has a viscosity at a temperature of 40 ° C. of 10 Pa · s or less as determined using a magnetic bearing rheometer using a 40 mm cone-plate measuring system at a shear rate of 0.1 1 / s. The present invention also provides an article comprising a reaction product of a photopolymerizable composition, which exhibits an elongation at break of at least 25%. In addition, the present invention provides a method of manufacturing an article comprising (i) providing a photopolymerizable composition and (ii) selectively curing the photopolymerizable composition to form an article. The method also optionally includes (iii) curing the unpolymerized urethane component and / or reactive diluent remaining after step (ii). In addition, receiving, by a manufacturing device having one or more processors, a digital object comprising data specifying an article； And creating an article based on a digital object, using a manufacturing device by a additive manufacturing process. A display that displays a 3D model of the article； And one or more processors for causing the 3D printer to create a physical object of the article in response to the 3D model selected by the user.본 발명은, 50 내지 90 중량%의 적어도 하나의 우레탄 성분, 5 내지 50 중량%의 적어도 하나의 반응성 희석제, 0.1 내지 5 중량%의 광개시제, 및 선택적으로 억제제를 포함하는 광중합성 조성물을 제공하며, 상기 조성물은 0.1 1/s의 전단 속도에서 40 mm 콘-플레이트 측정 시스템을 사용하는 자기 베어링 레오미터를 사용하여 결정할 때 40℃의 온도에서의 점도가 10 Pa·s 이하이다. 본 발명은 광중합성 조성물의 반응 생성물을 포함하는 물품을 또한 제공하는데, 이 물품은 25% 이상의 파단신율을 나타낸다. 또한, 본 발명은, (i) 광중합성 조성물을 제공하는 단계 및 (ii) 광중합성 조성물을 선택적으로 경화시켜 물품을 형성하는 단계를 포함하는, 물품의 제조 방법을 제공한다. 본 방법은 선택적으로 (iii) 단계 (ii) 후에 남아 있는 중합되지 않은 우레탄 성분 및/또는 반응성 희석제를 경화시키는 단계를 또한 포함한다. 또한, 하나 이상의 프로세서를 갖는 제조 디바이스에 의해, 물품을 특정하는 데이터를 포함하는 디지털 객체를 수신하는 단계； 및 적층 제조 공정에 의해 제