The present invention provides a superelastic alloy containing: 8.0-20.0 mass% of essential additive elements of Au and at least one of Cr and Mo, and an optional additive element of Ta and, as the remaining portion, Ti and unavoidable impurities, wherein the Cr equivalent calculated on the basis of the following formula representing the relationship among the Cr content, the Mo content, and the Ta content, is within the range of larger than 5.0 but smaller than 8.0. The alloy is an Ni-free superelastic alloy, and has good X-ray imaging properties. Therefore, the alloy is suitable for use in the medical field. Cr equivalent = [Cr content (mass%)] + ([Mo content (mass%)]/1.7) + ([Ta content (mass%)]/15)La présente invention concerne un alliage super-élastique contenant : de 8,0 à 20,0 % en masse déléments additifs essentiels de lAu et au moins un élément parmi le Cr et le Mo, et un élément additif facultatif du Ta, le reste étant du Ti et les inévitables impuretés, dans lequel léquivalent du Cr calculé sur la base de la formule suivante représentant la relation entre la teneur en Cr, la teneur en Mo, et la teneur en Ta, est dans la plage des valeurs supérieures ou égales à 5,0 mais inférieures à 8,0. Lalliage est un alliage super-élastique sans Ni, et il présente de bonnes propriétés dimagerie aux rayons X. Lalliage selon linvention convient de ce fait à une utilisation dans le domaine médical. Équivalent du Cr = [teneur en Cr (% en masse)] + ([teneur en Mo (% en masse)]/1,7) + ([teneur en Ta (% en masse)]/15)本発明は、必須の添加元素として、8.0質量%以上20.0質量%以下のAuと、CrとMoの少なくともいずれかとを含み、任意の添加元素としてTaを含み、残部がTi及び不可避不純物からなる超弾性合金であって、Cr含有量とMo含有量とTa含有量との関係について次式に基づき算出されるCr当量が、5.0超8.0未満の範囲内にある超弾性合金である。この合金は、Niフリーの超弾性合金であり、レントゲン造影性が良好である。そのため、この合金は医療分野に好適に使用可能である。 Cr当量=[Cr含有量(質量%)]+([Mo含有量(質量%)]/1.7)+([Ta含有量(質量%)]/15)