method of manufacturing three dimensional scaffolds polilaktydowych culture skin equivalents is characterized by the fact that polylactide in chloroform or methylene chloride solution with a concentration of 4 - 10 wt%. placed in a glass reactor and mixed to complete dissolution of the polymer.then the solution is added nierozpuszczalnik polylactide, which is methyl or ethyl alcohol in quantities of from 3 to 20% by weight, and mixed at a temperature of 20 to 25 degrees celsius to obtain a homogeneous solution, after which the alcohol alifatyczny c3 - c5, simple or branched, in quantities from 3 to 12 wt%. and still are mixed to obtain a homogeneous solution.the solution is on the substrate and dried. during the whole process of mixing is achieved by stirring volume 40 - 50% volume of polymer solution and at 550 to 700 rpm.Sposób wytwarzania trójwymiarowych rusztowań polilaktydowych do hodowli ekwiwalentów skóry charakteryzuje się tym, że roztwór polilaktydu w chloroformie lub dichlorometanie o stężeniu 4 - 10% wag. umieszcza się w reaktorze szklanym i miesza się do całkowitego rozpuszczenia polimeru. Następnie do roztworu dodaje się nierozpuszczalnik polilaktydu, którym jest alkohol metylowy lub etylowy w ilości od 3 do 20% wag., i miesza się w temperaturze od 20 do 25°C do uzyskania jednorodnego roztworu, po czym dodaje się alkohol alifatyczny C3-C5, prosty lub rozgałęziony, w ilości od 3 do 12% wag. i nadal miesza się do uzyskania jednorodnego roztworu. Roztwór wylewa się na podłoże i suszy. Podczas całego procesu mieszanie realizuje się za pomocą mieszadła o objętości 40 - 50% objętości roztworu polimeru i z prędkością 550 - 700 obr/min.