PROBLEM TO BE SOLVED: To provide a method for producing platy ceria particles capable of producing platy ceria particles having high monodisperse capacity, an average primary particle diameter of a sufficient size (e.g. 20 &mum or more) and high brightness.SOLUTION: The method for producing platy ceria particles contains a process for obtaining a mixed liquid by mixing a cerium nitrate solution and a sodium hydrogencarbonate solution in a solvent containing water so as to make cerium concentration to be 0.008-0.15 mol/L and sodium concentration to be 0.1-0.4 mol/L, a process for obtaining platy cerium carbonate octahydrate particles of single crystal having an average primary particle diameter of 20-100 &mum and an average thickness of 0.2-4 &mum by precipitating and growing cerium carbonate particles by maintaining the temperature of the mixed liquid within the range of 10-75°C for 20 hours or more, and a process for obtaining platy ceria particles by calcining the platy cerium carbonate octahydrate particles.COPYRIGHT: (C)2010,JPO&INPIT【課題】高い単分散性及び十分な大きさ(例えば20μm以上)の平均一次粒子径を有しており、高い光輝性を有する板状セリア粒子を製造することができる板状セリア粒子の製造方法を提供すること。【解決手段】硝酸セリウム溶液と炭酸水素ナトリウム溶液とを水を含有する溶媒中においてセリウム濃度が0.008~0.15mol/Lとなり且つナトリウム濃度が0.1~0.4mol/Lとなるように混合して混合液を得る工程と、前記混合液の温度を10~75℃の範囲内に20時間以上維持することにより炭酸セリウム粒子を析出及び成長せしめて、平均一次粒子径が20~100μmであり且つ平均厚みが0.2~4μmである単結晶の板状炭酸セリウム八水和物粒子を得る工程と、前記板状炭酸セリウム八水和物粒子を焼成して板状セリア粒子を得る工程と、を含むことを特徴とする板状セリア粒子の製造方法。【選択図】なし