The present invention relates to a deodorant composition for a building panel. The present invention comprises: a deodorant composition of 40-50 wt% of an inorganic ceramic binder obtained by mixing and stirring alkaline silicate which is any one of lithium, sodium, and potassium containing 20-30 wt% of silica and aqueous silica sol containing 40-50 wt% of silica having a particle size of 20-40 nm at a weight ratio of 7:3 or 6:4, and then heating and mixing the result for six hours at 50-60°C 20-30 wt% of an inorganic deodorant of one or more of charcoal, zeolite, tourmaline, jade, red clay, and tourmaline 5-10 wt% of an additive formed of polymethyl siloxane and 10-20 wt% of a solvent of one or more of methanol, isopropanol, normal butanol, and butyl cellosolve wherein 1-3 weight ratio of sodium hydroxide or potassium hydroxide is contained with respect to the total 100 weight ratio of the inorganic ceramic binder. The inorganic ceramic binder wherein the silica-containing alkaline silicate and the aqueous silica sol are mixed among the composition applied to construction panels is used to enhance the adhesion of the composition. Accordingly, peeling of the composition is unlikely, and the resistance to heat, waterproofness, and durability can be improved allowing the construction panels to be used outside of the building structures with little or no damage to the composition.COPYRIGHT KIPO 2015본 발명은 건축패널 인쇄용 탈취 조성물에 관한 것으로, 이산화규소를 20~30중량% 포함하는 리튬, 소디움, 포타슘 중 어느 하나의 알칼리성 실리케이트와, 20~40nm 입자크기로 이루어진 이산화규소를 40~50중량% 포함하는 수용성 실리카졸이 7:3의 중량비율이나 6:4의 중량비율로 혼합, 교반된 후, 50~60℃를 유지한 상태에서 6시간 동안 가열되어 혼합된 무기질세라믹바인더 40~50중량%, 숯, 제오라이트, 토르말린, 옥, 황토, 전기석 중 어느 하나 또는 둘 이상이 혼합되는 무기질 탈취제 20~30중량%, 폴리메틸실록산으로 이루어진 첨가제 5~10중량%, 메탄올, 이소프로판올, 노르말 부탄올, 부틸셀로솔브 중 어느 하나 이상으로 이루어진 용제 10~20중량%로 혼합된 탈취조성물로 이루어지되, 상기 무기질세라믹바인더의 전체 100 중량비율에 대하여 수산화나트륨이나 수산화칼륨 중 어느 하나가 1~3 중량비율이 포함되어 이루어진다.본 발명은 건축용 패널에 도장되는 조성물 중 이산화규소가 포함된 알칼리성 실리케이트와 수용성 실리카졸이 혼합된 무기질세라믹바인더를 통해 각각의 조성물 간의 부착력이 증가되어 건축용 패널에