A tampon pledget includes crosslinked cellulose fibers having microstructures treated to provide improved absorbency and higher wet strength. The fibers are treated with a crosslinking agent to provide at least one of a molecular weight between crosslinks of from about 10 to 200 and a degree of crystallinity of from about 25% to 75%. The crosslinking agent includes citric acid in 1% by weight. The crosslinking agent may further include sodium hypophosphite in 1% by weight. In another embodiment, the crosslinking agent may be a difunctional agent including a glyoxal or a glyoxal-derived resin. In still another embodiment, the crosslinking agent is a multifunctional agent including a cyclic urea, glyoxal, polyol condensate. The crosslinking agent is added in an amount from about 0.001% to 20% by weight based on a total weight of cellulose fibers to be treated and, preferably, in an amount of about 5% by weight.탐폰 거즈는 개선된 흡수성 및 보다 높은 습윤 강도를 제공하도록 처리된 미세구조를 갖는 가교결합된 셀룰로즈 섬유를 포함한다. 섬유를 가교결합제로 처리하여 약 10 내지 200의 가교결합 간의 분자량 및 약 25% 내지 75%의 결정화도 중의 적어도 하나를 제공한다. 가교결합제는 시트르산을 1중량%로 포함한다. 가교결합제는 차아인산나트륨을 1중량%로 추가로 포함할 수 있다. 또 다른 양태에서, 가교결합제는 글리옥살 또는 글리옥살-유도된 수지를 포함한 이관능성 제제일 수 있다. 여전히 또 다른 양태에서, 가교결합제는 사이클릭 우레아, 글리옥살, 폴리올 축합물을 포함하는 다관능성 제제이다. 가교결합제는, 처리하고자 하는 셀룰로즈 섬유의 총 중량을 기준으로 하여, 약 0.001 내지 20중량%의 양으로, 바람직하게는 약 5중량%의 양으로 첨가된다.