PROBLEM TO BE SOLVED: To provide a cosmetic containing a silica structure that can be easily industrially produced, and achieving both of light-scattering property and a good feeling in use.SOLUTION: The cosmetic comprises a silica nano structure, which is an aggregate of fiber-like or ribbon-like basic structures having a width or thickness of 5 to 100 nm and an aspect ratio of 2 or more. The silica nanostructure is obtained through steps of: associating a polymer having a straight-chain polyethylene imine skeleton in an aqueous medium obtaining a complex of the polymer and silica by adding alkoxysilane to the obtained associated polymer and calcining the complex to remove the polymer. The aggregate has a size (in a longest part of the aggregate when observed in a TEM image) ranging from 1 μm to 20 μm. Further, the cosmetic contains a material comprising the above silica nano structure and a metal oxide nano crystal having a size of 2 to 10 nm bonded to the surface of the fiber-like or ribbon-like silica.COPYRIGHT: (C)2013,JPO&INPIT【課題】 工業的生産が容易なシリカの構造体を含有する化粧品であって、光散乱性と使用時の好感覚とを両立できる化粧品を提供すること。【解決手段】 直鎖状ポリエチレンイミン骨格を有するポリマーを水性媒体中で会合させる工程、水性媒体の存在下で、得られたポリマーの会合体にアルコキシシランを加えることにより、前記ポリマーとシリカとの複合体を得る工程、これを複合体を焼成し、ポリマーを除去する工程で得られた、太さ又は厚みが5~100nmでアスペクト比が2以上のファイバー状又はリボン状の基本構造体の集合体であって、該集合体の大きさ(TEM画像で観測したときの、最も長い部分)が1μm~20μmの範囲であるシリカナノ構造体を含有してなることを特徴とする化粧品、さらには。前記シリカナノ構造体のファイバー状またはリボン状のシリカ表面に、2~10nmの大きさの金属酸化物ナノ結晶が結合しているものを含有する化粧品【選択図】 図10