The invention relates to a process for preparing biocomposites based on cellulose acetate and anionic clays intended to be used as controlled release systems for medicaments. According to the invention, the process consists in dispersing the cellulose acetate into acetone, in a ratio of 1:4, stirring the mixture for 4 h, admixing the anionic clay as powder in a cellulose acetate : anionic clay ratio of 10 : 0.75...1.5, the mixture being then stirred for 24 h for homogenization and afterwards poured as a film on a flat surface, dried at a temperature of 60°C for 1 h, to result in a biocomposite having a thickness of 500...550 &mu m, a porosity of 70...70%, a pore size of 0.02...0.14 &mu m and resistant to media having a pH value of 6...13.Invenţia se referă la un procedeu de obţinere a unor biocompozite pe bază de acetat de celuloză şi argile anionice, utilizate ca sisteme de eliberare controlată de medicamente. Procedeul conform invenţiei constă din aceea că acetatul de celuloză se dispersează în acetonă într-un raport 1 : 4, se agită amestecul timp de 4 h, după care se adaugă argila anionică pulbere într-un raport acetat de celuloză : argilă de 10 : 0,75...1,5, după care amestecul se agită, pentru omogenizare, timp de 24 h, apoi se toarnă sub formă de film pe o suprafaţă plană, se usucă la o temperatură de 60°C, timp de 1 h, din care rezultă un biocompozit având o grosime de 500...550 μ m, o porozitate de 70...70%, o dimensiune a porilor de 0,02...0,14 μ m şi o rezistenţă în medii cu pH de 6...13.