PROBLEM TO BE SOLVED: To provide an iodine quick release material having a high iodine release speed and capable of preparing aqueous iodine for use in disinfection in an extremely short time when brought into contact with water, and to provide its manufacturing method.SOLUTION: The iodine quick discharge material is manufactured by impregnating a polyvinyl acetal-based porous material having an acetalization degree of 50-90 mol% with 1-50 wt.% of at least one kind of a wetting agent selected from the group consisting of glycerine, ethylene glycol, polyethylene glycol, etc., and hermetically sealing solid iodine in an amount of 10-400 wt.% with respect to the porous material, in a container along with the impregnated porous material to be heated at 30-100°C.COPYRIGHT: (C)2009,JPO&INPIT【課題】ヨウ素放出速度が速く、水と接触させたときに極めて短時間で消毒に用いうるヨウ素水を調製することができるヨウ素迅速放出材およびその製造方法を提供すること。【解決手段】アセタール化度50~90モル%のポリビニルアセタール系多孔質体に、該多孔質体に対して1~50重量%の、グリセリン、エチレングリコール、ポリエチレングリコール、等より選択される1種以上の湿潤剤を含浸させ、前記多孔質体に対して10~400重量%の固体ヨウ素を、前記含浸後の多孔質体とともに容器内に密閉し、30~100℃で加熱することを特徴とするヨウ素迅速放出材の製造方法。【選択図】なし