PROBLEM TO BE SOLVED: To provide a method of manufacturing a biomedical electrode used for iontophoresis or the like, which achieves cost reduction without causing deformation or the like in a thin plastic base material even when a conductive layer is formed, or the like.SOLUTION: A method of manufacturing a biomedical electrode 1 includes: a preparation step of a flexible base material 2 a step of forming a metal electrode 11 composed of a metal deposition film on the flexible base material 2 and a step of forming a metal chloride electrode 21 composed of a metal chloride film adjacent to the same surface S of the flexible base material 2 where the metal electrode 11 is formed, and the thickness of the metal electrode 11 is made thinner than the thickness of the metal chloride electrode 21. It is preferable that the metal electrode 11 is a silver electrode and that the metal chloride electrode 21 is a silver-silver chloride electrode. It is preferable to have a formation step of a primer layer between the preparation step of the flexible base material 2 and the formation step of the metal electrode 11, and have a formation step of a film for liftoff between the formation step of the primer layer and the formation step of the metal electrode 11.COPYRIGHT: (C)2013,JPO&INPIT【課題】導電層を形成しても薄いプラスチック基材に変形等が生じることなく、コスト低減を実現したイオントフォレシス等に用いる生体用電極の製造方法等を提供する。【解決手段】フレキシブル基材2の準備工程と、フレキシブル基材2上に金属蒸着膜からなる金属電極11を形成する工程と、金属電極11が形成されるフレキシブル基材2の同一面Sに隣接して金属塩化物膜からなる金属塩化物電極21を形成する工程とを有し、金属電極11の厚さを金属塩化物電極21の厚さよりも薄くしてなる生体用電極1の製造方法により上記課題を解決した。金属電極11が銀電極であり、金属塩化物電極21が銀-塩化銀電極であることが好ましい。フレキシブル基材2の準備工程と金属電極11の形成工程との間にプライマー層の形成工程を有し、プライマー層の形成工程と金属電極11の形成工程との間にリフトオフ用膜の形成工程を有することが好ましい。【選択図】図1