Procedure for obtaining a material for the constitution of an osteomimetic endoosseous implant for medical or veterinary use, characterized in that it comprises the steps consisting of: i. obtain (210) a homogeneous mixture consisting of a biocompatible thermoplastic polymer and tricalcium phosphate in beta form (ß TCP), iv. incorporate (216) into the adenosine monophosphate mixture ii. subjecting said mixture to a molding operation (220) by injection or extrusion by means of a screw machine, at an injection temperature at least equal to the melting temperature of said polymer and a pressure between 70 MPa and 140 MPa to transform said tricalcium phosphate in a non-stoichiometric calcium apatite 3 (Ca3 (PO4) 2) (OH) 2Ca similar to that of bone.Procedimiento para obtener un material para la constitución de un implante osteomimético endoóseo de uso médico o veterinario, caracterizado porque comprende las etapas que consisten en: i. obtener (210) una mezcla homogénea que consiste en un polímero termoplástico biocompatible y fosfato tricálcico en forma beta (ß TCP), iv. incorporar (216) a la mezcla de monofosfato de adenosina ii. someter dicha mezcla a una operación de moldeo (220) por inyección o extrusión mediante una máquina de tornillo, a una temperatura de inyección al menos igual a la temperatura de fusión de dicho polímero y una presión de entre 70 MPa y 140 MPa para transformar dicho fosfato tricálcico en una apatita de calcio no estequiométrica 3(Ca3(PO4)2)(OH)2Ca similar a la del hueso.