The present invention provides a dental member which has a reduced size and therefore does not damage a tooth root upon implantation thereof, has high strength and low elasticity, and exhibits excellent engraftment stability after implantation thereof.The dental member is produced from an amorphous alloy having a chemical composition represented by the formula: ZraNibCucAld [wherein each of a, b, c and d represents a value of at.%, wherein a represents 60 to 75 at.%, b represents 11 to 30 at.%, c represents 1 to 16 at.%, and d represents 5 to 20 at.%]. The dental member can be used as an orthodontic anchor screw which has a screw part having a core diameter of 0.5 to 1.0 mm or having a length of 2 to 5 mm, a one-piece dental implant which has a screw part having a largest diameter of 0.5 to 2.9 mm and a length of 2 to 13.4 mm, or a two-piece dental implant which has a screw part having a largest diameter of 0.5 to 2.9 mm and a length of 2 to 5.9 mm.La présente invention concerne un élément dentaire qui présente une taille réduite, et par conséquent n'endommage pas une racine dentaire lors de son implantation, possède une résistance élevée et une faible élasticité, et présente une excellente stabilité de prise de greffe après son implantation. L'élément dentaire est produit à partir d'un alliage amorphe ayant une composition chimique représentée par la formule : ZraNibCucAld [où chacun des nombres a, b, c et d représente une valeur en % atomique, où a représente 60 à 75 % atomiques, b représente 11 à 30 % atomiques, c représente 1 à 16 % atomiques, et d représente 5 à 20 % atomiques]. L'élément dentaire peut être utilisé sous la forme d'une vis d'ancrage orthodontique qui comporte une partie de vis de diamètre de cœur compris entre 0,5 et 1,0 mm ou de longueur comprise entre 2 à 5 mm, d'un implant dentaire monobloc qui comporte une partie de vis de plus grand diamètre compris entre 0,5 et 2,9 mm et de longueur comprise entre 2 et 13,4 mm, ou d'un implant dentaire e