Provided is an antibacterial flooring coated with a film in which an antibacterial precious metal component is distributed at a high concentration over the entire film or on the surface portion of the film. A flooring material according to the present invention is formed by applying, drying, polymerizing and curing an antibacterial flooring paint including a resin raw material, a precious metal salt and a fulvic acid, and is characterized in that 10-7-10-4 [mol/kg of the flooring material] of the precious metal salt is included with respect to 1 kg of the flooring material and the molar equivalent ratio of the precious metal salt to a carboxyl group of the fulvic acid in the flooring material is within a range of 1:10 to 1:100.Linvention concerne un revêtement de sol antibactérien revêtu dun film dans lequel un composant de métal précieux antibactérien est réparti à une concentration élevée sur la totalité du film ou sur la partie superficielle du film. Un matériau de revêtement de sol selon la présente invention est formé par application, séchage, polymérisation et durcissement dune peinture de revêtement de sol antibactérien comprenant un matériau brut à base de résine, un sel de métal précieux et un acide fulvique, et est caractérisé en ce quune quantité comprise entre 10-7 et 10-4 [mol/kg du matériau de revêtement de sol] du sel de métal précieux est incluse par rapport à 1 kg du matériau de revêtement de sol et le rapport équivalent molaire entre le sel de métal précieux et un groupe carboxyle de lacide fulvique dans le matériau de revêtement de sol se situe dans une plage allant de 1:10 à 1:100.貴金属抗菌成分を塗膜全体又は塗膜の表面部分に高濃度に分布させた抗菌性床面を提供する。樹脂原料と、貴金属塩と、フルボ酸と、を含むフローリング用抗菌性塗料を、塗布、乾燥、及び重合硬化させて形成した床材であって、該床材の重量1kgに対して、前記貴金属塩を、10-7乃至10-4[モル/kg床材]含み、前記床材中の前記貴金属塩のモル当量と、フルボ酸のカルボキシル基当量と、の比が、1:10乃至1:100の範囲内であることを特徴とする。