Conventional copper pyrithione products have been considered to be too fast to dissolve in seawater in tropical waters, and the development of copper pyrithione having a large average particle diameter has also been required in order to make the dissolution into seawater slower. In addition, until now, copper pyrithione products are likely to be powdered at the worksite, and once inhaled into the lungs, the bedding crystals have been anxious about their health. By using the inorganic copper (II) -inorganic ammonium complex salt instead of the inorganic copper (II) salt as a conventional raw material for production, the resulting small particles of copper pyrithione are made into a large granular aggregate having an average particle diameter of 9-13 μm , Both of which were solved simultaneously.종래의 구리 피리티온 제품은 열대해역에서는 해수에의 용출이 너무 빠르다고 생각되어왔고, 해수에의 용출을 더 느리게 하도록 하기 위해, 또한 큰 평균입자직경을 갖는 구리 피리티온의 개발이 요구되어 왔다. 또한, 지금까지의 구리피리티온제품은 작업현장에서 가루되기 쉬어, 일단 폐로 흡입되면 그 침상결정때문에 건강에의 불안이 나타나고 있었다. 종래의 제조원료인 무기구리(II)염의 대신에 무기구리(II)·무기암모늄복합염을 이용해서, 생성한 작은 입자의 구리피리티온을 평균입자 직경 9-13μm의 큰 입상집합체로 하는 것에 의해, 상기 두 과제를 동시에 해결하였다.