PROBLEM TO BE SOLVED: To provide a new calcium phosphate-based compound which exhibits a unique property change not found in a conventional calcium phosphate-based compound.SOLUTION: A calcium phosphate-based compound is synthesized by heating at 80-100°C an aqueous solution, in which 1.9-2.1 M calcium nitrate tetrahydrate and 1.1-1.3 M ammonium dihydrogen phosphate are contained so that a molar ratio of calcium to phosphorus (Ca/P) is 1.6-1.7. The obtained calcium phosphate-based compound is a composite material including calcium nitrate, ammonium nitrate, calcium dihydrogen phosphate, and calcium hydrogen phosphate, and has a structure where calcium phosphate-based particles are distributed in the calcium nitrate. The obtained calcium phosphate-based compound is made into a bulk body state at lower than 35°C, made into a wet state in a high humidity atmosphere, and made into a slurry state when heated to 40°C or higher, and the bulk body state, the wet state, and the slurry state are reversibly changed according to the atmosphere.COPYRIGHT: (C)2014,JPO&INPIT【課題】従来のリン酸カルシウム系化合物にはみられない特異な性状変化を示す、新規なリン酸カルシウム系化合物を提供する。【解決手段】リンとカルシウムのモル比(Ca/P)が1.6~1.7となる範囲で、1.9~2.1Mの硝酸カルシウム四水和物と、1.1~1.3Mのリン酸二水素アンモニウムとを含む水溶液を、80~100℃に加熱して合成する。これにより得られたリン酸カルシウム系化合物は、硝酸カルシウム、硝酸アンモニウム、リン酸二水素カルシウム、及びリン酸水素カルシウムを含む複合材料であって、硝酸カルシウムの中にリン酸カルシウム系粒子が分布する構造を持つ。35℃未満ではバルク体状であり、多湿雰囲気下では湿潤状態化し、40℃以上に加熱するとスラリー状となり、これらバルク体状、湿潤状態、スラリー状の各状態が雰囲気に応じて可逆的に変化する。【選択図】図1