The present invention relates to a method for manufacturing a zirconia implant drill, the method comprising the steps of: injecting and molding a raw material containing a zirconia powder or injecting a raw material containing a zirconia together with a liner in a molding frame calcining the molded result performing a marking step of coating a color oxide solution on the calcined result to form a plurality of color bands exhibiting height information in a direction vertical to the length of the calcined result sintering the marked result and polishing the sintered result to form an implant drill including a sank portion and a drill blade portion. According to the present invention, a zirconia implant drill can be obtained that has excellent chemical resistance and corrosion resistance, no allergy, excellent cutting efficiency at the implanting work due to excellent wear resistance, less frictional heat due to the low friction coefficient, thereby suppressing the secondary damage to bone tissues, and increased usability effectiveness through marking without a strength decrease.COPYRIGHT KIPO 2016본 발명은, 지르코니아 분말을 포함하는 원료를 몰드에 주입하여 성형하거나, 지르코니아 분말을 포함하는 원료를 이장재와 함께 성형틀에 주입하여 성형하는 단계와, 성형된 결과물을 하소하는 단계와, 하소 결과물에 색상 산화물 용액을 도포하여 상기 하소 결과물의 길이에 수직한 방향에 높이 정보를 나타내는 복수의 색상띠를 형성하는 마킹 공정을 수행하는 단계와, 마킹이 이루어진 결과물을 소결하는 단계 및 소결된 결과물을 연마하여 생크부와 드릴날부를 포함하는 임플란트 드릴을 형성하는 단계를 포함하는 지르코니아 소재의 임플란트 드릴 제조방법에 관한 것이다. 본 발명에 의하면, 내화학성 및 내부식성이 우수하고, 알러지 현상과 같은 부작용이 없으며, 내마모성이 우수하여 매식 작업 시에 절삭 효율이 우수하고, 마찰계수가 낮아 마찰열이 적게 발생하여 골조직에 대한 2차 피해가 억제되며, 강도 저하 없는 마킹에 의해 사용성 유효성이 증대된 지르코니아 소재의 임플란트 드릴을 얻을 수가 있다.