The present invention relates to a method of preparing a thermally-gelling hypromellose hard capsule having improved storage stability, film strength, film distribution, filling performance, and bioavailability and, more specifically, to a method of preparing a thermally gelling hypromellose hard capsule having improved storage stability, film strength, film distribution, filling performance, and bioavailability, which comprises the steps of: adding and dissolving 0.1-0.5 parts by weight of a plasticizer, 0.1-0.5 parts by weight of a wetting agent, and a small amount of a viscosity stabilizer, based on 100 parts by weight of a hypromellose aqueous solution, in which 19-22 parts by weight of hypromellose is dissolved in purified water, sequentially and suitably so as to control viscosity； and pre-heating a temperature of a mold pin to 100-120°C, depositing the pre-heated mold pin in an immersion liquid bath in which the hypromellose aqueous solution is maintained at a temperature of 19-21°C, and molding and drying the mold pin.본 발명은 보관 안정성, 피막 강도, 필름 분포도, 충전성 및 생체 이용률을 개선시킨 열겔화 히프로멜로오스 하드 캡슐의 제조방법에 관한 것이다. 더욱 상세하게는 히프로멜로오스 19-22 중량부를 정제수에 용해시킨 히프로멜로오스 수용액 100 중량부에 대해 0.1~0.5 중량부의 가소제, 0.1~0.5 중량부의 습윤제, 소량의 점도 안정화제를 적정량 순차적으로 첨가 용해시켜 점도를 조절시킨 후 몰드핀의 온도를 100~120℃로 예열시킨 후 히프로멜로오스 수용액의 온도가 19~21℃로 유지되는 침액조에 예열된 몰드핀을 침적하여 성형 건조시켜 보관 안정성, 피막 강도, 필름 분포도, 충전성 및 생체 이용률을 개선시킨 열겔화 히프로멜로오스 하드 캡슐의 제조방법에 관한 것이다.