Provided are hypromellose acetate succinate (HPMCAS) having such a property that a solution of the HPMCAS in a solvent has a controlled viscosity and a manufacturing method thereof. More specifically, provided is hypromellose acetate succinate having such property that a solution of 10 parts by weight of the hypromellose acetate succinate in 100 parts by weight of a mixed solvent, which has a weight ratio of methylene chloride to methanol of 1:1 and a viscosity of the solution at 20°C of 135 mPa·s or less. Moreover, provided is a hypromellose acetate succinate manufacturing method including: an esterification process of obtaining a reaction solution by adding acetic anhydride and succinic anhydride to a solution of hypromellose in glacial acetic acid in the presence of sodium acetate, wherein the succinic anhydride is added intermittently and a precipitation step of mixing the reaction solution with water to precipitate the hypromellose acetate succinate.COPYRIGHT KIPO 2018용매에 용해시켰을 때에 용액의 점도가 제어된 HPMCAS 및 그의 제조 방법을 제공한다. 구체적으로는, 히프로멜로오스아세트산에스테르숙신산에스테르 10질량부를, 염화메틸렌과 메탄올의 질량비 1:1의 혼합 용매 100질량부에 용해시킨 용액의 20℃에 있어서의 점도가 135mPa·s 이하인 히프로멜로오스아세트산에스테르숙신산에스테르를 제공한다. 또한, 히프로멜로오스의 빙초산 용액에, 아세트산나트륨 존재 하에서, 무수 아세트산 및 무수 숙신산을 첨가하여 반응액을 얻는 에스테르화 공정이며, 상기 무수 숙신산이 2회 이상에 걸쳐 첨가되는 에스테르화 공정과, 상기 반응액과 물을 혼합하여 히프로멜로오스아세트산에스테르숙신산에스테르를 석출시키는 석출 공정을 적어도 포함하는 이 히프로멜로오스아세트산에스테르숙신산에스테르의 제조 방법을 제공한다.