The present invention relates to a method for manufacturing a porous metal support coated with a porous oxide film and a porous metal support produced thereby. More particularly, the present invention provides a method of forming a porous oxide film by an anodic oxidation process using an electrolytic solution in which an alcohol solvent is added to a surface of a porous metal body produced by a freeze casting process. Accordingly, the present invention can increase the fluidity of the electrolytic solution due to the alcohol solvent in the electrolytic solution, thereby forming a porous oxide film to the inside of the pores, and the sediment can not be accumulated in the pores even after the anodic oxidation process, so that the decrease in the porosity can be controlled. In addition, the porous metal scaffold has high biocompatibility, and cell proliferation can be smoothly performed, and the porous metal scaffold can be applied as an implant.본 발명은 다공성 산화 피막이 코팅된 다공성 금속 지지체 제조방법 및 이에 의해 제조된 다공성 금속 지지체에 관한 것이다. 더욱 상세하게는 동결 주조 공정으로 제조된 금속 다공체 표면에 알코올 용매가 첨가된 전해액을 이용한 양극 산화 공정으로 다공성 산화 피막을 형성하는 제조방법을 제공한다. 따라서 본 발명은 전해액 내에 알코올 용매로 인해 전해액의 유동성을 증가되어, 기공 내부까지 다공성 산화 피막을 형성할 수 있고, 양극 산화 공정 후에도 침전물이 기공 내에 쌓이지 않아 기공률의 저하가 제어될 수 있다. 또한, 상기 다공성 금속 지지체는 높은 생체 적합성을 가져서 세포의 증식이 원활하게 이루어질 수 있으며, 임플란트로 응용될 수 있다.