An alpha/beta titanium alloy comprising, in percent by weight based on total alloy weight: 3.9 to 4.5 aluminum； 2.2 to 3.0 vanadium； 1.2 to 1.8 iron； 0.24 to 0.30 oxygen； up to 0.08 carbon； up to 0.05 nitrogen； up to 0.015 hydrogen； titanium； and up to a total of 0.30 of other elements. A non-limiting embodiment of the alpha/beta titanium alloy comprises an aluminum equivalent value in the range of 6.4 to 7.2, exhibits a yield strength in the range of 120 ksi (827.4 MPa) to 155 ksi (1,069 MPa), exhibits an ultimate tensile strength in the range of 130 ksi (896.3 MPa) to 165 ksi (1,138 MPa), and exhibits a ductility in the range of 12 to 30 percent elongation.Una aleación de titanio alfa/beta que comprende, en por ciento en peso basado en el peso total de la aleación: 3.9 a 4.5 de aluminio； 2.2 a 3.0 de vanadio； 1.2 a 1.8 de hierro； 0.24 a 0.30 de oxígeno； hasta 0.08 de carbono； hasta 0.05 de nitrógeno； hasta 0.015 de hidrógeno； titanio； y hasta un total de 0.30 de otros elementos. Una modalidad no limitante de la aleación de titanio alfa/beta comprende un valor de aluminio equivalente en el intervalo de 6.4 a 7.2, exhibe un límite de elasticidad en el intervalo de 120 ksi (827.4 MPa) a 155 ksi (1,069 MPa), exhibe una resistencia máxima a la tracción en el intervalo de 130 ksi (896.3 MPa) a 165 ksi (1,138 MPa), y exhibe una ductilidad en el intervalo de 12 a 30 por ciento de alargamiento.