An alpha/beta titanium alloy comprising, in percent by weight based on total alloy weight: 3.9 to 4.5 aluminum 2.2 to 3.0 vanadium 1.2 to 1.8 iron 0.24 to 0.30 oxygen up to 0.08 carbon up to 0.05 nitrogen up to 0.015 hydrogen titanium and up to a total of 0.30 of other elements. A non-limiting embodiment of the alpha/beta titanium alloy comprises an aluminum equivalent value in the range of 6.4 to 7.2, exhibits a yield strength in the range of 120 ksi (827.4 MPa) to 155 ksi (1,069 MPa), exhibits an ultimate tensile strength in the range of 130 ksi (896.3 MPa) to 165 ksi (1,138 MPa), and exhibits a ductility in the range of 12 to 30 percent elongation.Linvention porte sur un alliage de titane alpha/bêta comprenant, en pourcentage en poids sur la base du poids total de lalliage : 3,9 à 4,5 % daluminium 2,2 à 3,0 % de vanadium 1,2 à 1,8 % de fer 0,24 à 0,30 % doxygène jusquà 0,08 % de carbone jusquà 0,05 % dazote jusquà 0,015 % dhydrogène du titane et jusquà un total de 0,30 % dautres éléments. Un mode de réalisation non limitatif de lalliage de titane alpha/bêta comprend une valeur équivalente daluminium dans la plage de 6,4 à 7,2, présente une limite délasticité conventionnelle dans la plage de 120 ksi (827,4 MPa) à 155 ksi (1 069 MPa), présente a une résistance à la traction dans la plage de 130 ksi (896,3 MPa) à 165 ksi (1 138 MPa) et présente une ductilité dans la plage de 12 à 30 pour cent dallongement.