PROBLEM TO BE SOLVED: To provide a medium using a bark and a carbide, without using a chemical synthesized material, and capable of being produced with a simple process, a compact using the medium, and a producing method thereof.SOLUTION: Bark is fermented at a temperature range of 35 to 45°C for 7 to 8 months to produce organic carbon fiber through carbonization. The organic carbon fiber is cut into a length of 25 mm or shorter, immersed in water, and then packed in a formwork to be compacted for forming of a compact applicable to a medium. During the immersion in water, a component functioning as adhesive such as water soluble resin contained in the bark fiber is eluted to cover the surface of the bark fiber, so that strength of the compact can be ensured. Since a fiber derived from cellulose and a porous carbide are coexisted in the medium produced by using the method, the medium has high porosity and high permeability of water and air, and the growth promotion effect of carbide and the effect of inhibiting pathogenic propagation can be utilized. Consequently, the medium of the present invention is extremely useful as a medium.COPYRIGHT: (C)2014,JPO&INPIT【課題】 化学的に合成された材料を用いることなく、しかも簡便な工程で製造可能な、樹皮及び炭化物を用いた培地と当該培地を用いた成形体、及びそれらの製造方法を提供する。【解決手段】 樹皮を35~45℃の温度範囲で、7~8箇月間発酵させて炭化することにより得られる有機炭素繊維を、25mm以下の長さに切断し、水に浸漬してから、型枠に充填し、加圧成形して培地として使用可能な成形体を得る。水に浸漬することにより、樹皮繊維に含まれる、水溶性樹脂などの接着剤として機能する成分が溶出して、樹皮繊維表面を被覆し、成形体の強度を確保できる。また、前記の方法で得られた培地は、セルロースからなる繊維や多孔質の炭化物が混在しているので、空隙率が大きく、水や空気の透過性に富み、炭化物の成長促進作用及び病原菌の繁殖抑制作用が利用できるので、培地として極めて有用である。【選択図】なし