Various systems, devices, and methods for improved bone fixation are disclosed. The system includes a bone plate and a plurality of variable angle screws. The bone plate comprises titanium and the variable angle screws comprise a TiMo alloy treated to have a hardness of at least 35 HRC. A method of manufacturing an implant is also disclosed. The method includes machining the TiMo alloy having a first hardness value and a first % elongation to form an implant； heat treating, quenching, and aging the bone fastener to have a second hardness value that can be greater than the first hardness value and a second % elongation that can be both less than the first % elongation and greater than about 3% elongation.L'invention concerne divers systèmes, dispositifs et procédés pour une fixation osseuse améliorée. Le système comprend une plaque osseuse et une pluralité de vis à angle variable. La plaque osseuse comprend du titane et les vis à angle variable comprennent un alliage TiMo, traité afin d'obtenir une dureté d'au moins 35 HRC. L'invention concerne également un procédé de fabrication d'un implant. Le procédé comprend l'usinage de l'alliage TiMo ayant une première valeur de dureté et un premier % d'allongement pour former un implant ； le traitement thermique, le trempage et le vieillissement de la fixation osseuse afin d'obtenir une seconde valeur de dureté, qui peut être supérieure à la première valeur de dureté, et un second % d'allongement, qui peut être à la fois inférieur au premier % d'allongement et supérieur à environ 3 % d'allongement.