A process for reducing the rate of deterioration of wood that includes contacting the wood with an aqueous alkanline colloidal silicon-containing slat composition that is supersaturated with a boron-containing salt. The contacting may be at ambient or elevated temperature and pressure. The composition is an aqueous colloidal silicon-containing salt that is supersaturated with a boron-containing salt and optionally includes an aluminum salt and a preservative. The composition is made by mixing the boron-containing salt with a colloidal, aqueous mixture of a silicon-containing salt and optionally adding the aluminum salt and the preservative. The process is performed under conditions that result in a supersaturated solution of the boron-containing salt. Wood treated with the composition appears to be resistant to insects, rot, UV deterioration, fire, and other environmental insults. The wood also appears to have increased strength.Un procedimiento para reducir la velocidad de deterioro de madera que incluye poner en contacto la madera con una composición de sal que contiene silicio coloidal alcalina acuosa que se supersatura con una sal que contiene boro el contacto puede ser a temperatura y presión ambiente o elevada la composición es una sal que contiene silicio coloidal acuoso que se supersatura con una sal que contiene boro y opcionalmente incluye una sal de aluminio y un conservador la composición se elabora al mezclar la sal que contiene boro con una mezcla acuosa coloidal de una sal que contiene silicio y opcionalmente agregando la sal de aluminio y el conservador el procedimiento se realiza bajo condiciones que dan como resultado una solución supersaturada de la sal que contiene boro la madera tratada con la composición parece ser resistente a insectos, descomposición, deterioro por UV, fuego, y otros peligros ambientales la madera también parece tener una resistencia incrementada.