FIELD: metallurgy.SUBSTANCE: method comprises thermodiffusion hydrogen saturation of the implant and vacuum annealing. Before thermodiffusion hydrogen saturation and vacuum annealing, a porous coating is applied on the surface of the implant by diffusion welding with the help of welding of titanium alloy fibres at a temperature of 850-950°C to the surface of the implant from titanium alloys, hydrogen saturation is carried out at a temperature of 600-650°C to a hydrogen concentration of 0.5-0.8 wt %, and the subsequent vacuum annealing - to a hydrogen concentration of not more than 0.008 wt %.EFFECT: shearing force of the coating is increased from the monolithic substrate while maintaining its structure and properties.4 cl, 1 dwg, 1 tbl, 8 exИзобретение относится к металлургии, а именно к способам получения имплантатов из титановых сплавов с остеоинтегрирующим покрытием. Способ получения высокопористого остеоинтегрирующего покрытия на имплантатах из титановых сплавов включает термодиффузионное водородное насыщение имплантата и вакуумный отжиг. Перед термодиффузионным водородным насыщением и вакуумным отжигом на поверхность имплантата диффузионной сваркой наносят пористое покрытие путем приварки при температуре 850-950°С к поверхности имплантата из титановых сплавов волокон из титанового сплава, водородное насыщение проводят при температуре 600-650°С до концентрации водорода 0,5-0,8 мас. %, а последующий вакуумный отжиг - до концентрации водорода не более 0,008 мас. %. Повышается усилие среза покрытия с монолитной основы при сохранении ее структуры и свойств. 3 з.п. ф-лы, 1 ил., 1 табл., 8 пр.