The present invention provides a method for stably producing a particulate water absorbent which has high water absorption rate, while containing a polyacrylic acid (salt). A method for producing a particulate water absorbent according to the present invention comprises a polymerization step, a gel coarse grinding step (D50 is from 500 μm to 10 cm), a gel grinding step (D50' is from 360 μm to 1,500 μm； PDCR is from 0.02 to 0.10), a drying step and a surface crosslinking step. With respect to this method for producing a particulate water absorbent, the ratio of the nonvolatile component of a hydrous gel to the total weight of the hydrous gel is from 10% by weight to 48% by weight； and the CRC of the particulate water absorbent is 32.0 g/g or more.La présente invention concerne un procédé de production stable d'un absorbant d'eau particulaire qui présente un taux d'absorption d'eau élevé, tout en contenant un acide polyacrylique (ou un sel de celui-ci). Un procédé de production d'un absorbant d'eau particulaire selon la présente invention comprend une étape de polymérisation, une étape de broyage grossier de gel (D50 va de 500 µm à 10 cm), une étape de broyage de gel (D50' va de 360 µm à 1 500 µm ； PDCR est de 0,02 à 0,10), une étape de séchage et une étape de réticulation de surface. En ce qui concerne ce procédé de production d'un absorbant d'eau particulaire, le rapport du composant non volatil d'un gel aqueux au poids total du gel aqueux va de 10 % en poids à 48 % en poids ； et le CRC de l'absorbant d'eau particulaire est de 32,0 g/g ou plus.吸水倍率が高い、ポリアクリル酸（塩）を含む粒子状吸水剤の、安定的な製造方法を提供する。粒子状吸水剤の製造方法は、重合工程と、ゲル粗砕（Ｄ５０；５００μｍ～１０ｃｍ）工程と、ゲル粉砕（Ｄ５０'；３６０μｍ～１５００μｍ、ＰＤＣＲ；０．０２～０．１０）工程と、乾燥工程と、表面架橋工程と、を含み、含水ゲルの不揮発成分率が、含水ゲルの総重量に対して１０重量％～４８重量％であり、粒子状吸水剤のＣＲＣが３２．０ｇ／ｇ以上である方法である。