The present invention relates to a process for preparing calcium zincate crystals and comprises at least the following steps: (1) mixing calcium hydroxide (Ca (OH) 2 ) and zinc oxide (ZnO), one of its precursors, And water to a so-called starting suspension, wherein the mass ratio of one of the water: calcium hydroxide and zinc oxide, or a precursor thereof, or a mixture thereof, is at least 1, preferably from 2 to 15 and in particular from 3 to 5； (2) pulverizing the starting suspension in a three-dimensional wet microball mill at an ambient temperature of 50 DEG C or less at a residence time of 15 minutes or less, particularly a residence time in the range of 5 to 25 seconds； (3) recovering a suspension of calcium zincate crystals at the outlet of the pulverizer； And (4) optionally, concentrating or drying the suspension of calcium zincate crystals to obtain a powder of calcium zincate crystals. The present invention also relates to uses related to calcium zincate crystals obtained according to the method described above.본 발명은 아연산염칼슘 결정체를 제조하는 방법에 관한 것으로서, 적어도 다음의 단계들을 포함한다: (1) 수산화칼슘(Ca(OH)2) 및 산화아연(ZnO), 그의 전구체 중 하나, 또는 그것들의 혼합물 중 하나와, 물을 소위 출발 현탁액으로 만드는 단계 - 물: 수산화칼슘 및 산화아연, 또는 이들의 전구체 또는 이들의 혼합물 중 하나의 질량비는 1 이상, 바람직하게는 2 내지 15 및 특히 3 내지 5임 - ； (2) 상기 출발 현탁액을 50℃ 이하의 주변온도에서 3차원 습식 마이크로볼 분쇄기에서 15분 이하의 체류시간, 특히 5 내지 25초 범위의 체류시간 동안 분쇄하는 단계； (3) 상기 분쇄기의 출구에서 아연산염칼슘 결정체의 현탁액을 회수하는 단계； 및 (4) 선택적으로, 아연산염칼슘 결정체의 분말을 얻기 위하여 상기 아연산염칼슘 결정체의 현탁액을 농축하거나 건조하는 단계. 본 발명은 또한 상기에서 설명된 방법에 따라 얻어진 아연산염칼슘 결정체와 관련된 용도에 관한 것이다.