Provided is a simple method for manufacturing a glass container having high chemical durability without introducing a special processing step or processing equipment. The present invention includes a glass container manufacturing step for molding a glass tube under heating and obtaining a glass container, a cleaning step for cleaning the inside surface of the glass container obtained in the glass container manufacturing step using a cleaning liquid comprising water, an acid aqueous solution, a surfactant aqueous solution, or an aqueous solution of an acid to which a surfactant is added, and a strain removal step for heating and increasing the temperature of the glass container cleaned in the cleaning step and subsequently cooling the glass container to remove strain therefrom, the temperature of the glass container being 30-150°C and the cleaning time being 10-15 seconds in the cleaning step, and the maximum atmospheric temperature in the strain removal step being controlled so as to be 650-670°C.L'invention concerne un procédé simple de fabrication d'un récipient en verre ayant une durabilité chimique élevée sans l'introduction d'une étape de traitement spéciale ou d'un équipement de traitement spécial. La présente invention comprend une étape de fabrication d'un récipient en verre permettant de mouler un tube en verre sous chauffage et d'obtenir un récipient en verre, une étape de nettoyage permettant de nettoyer la surface intérieure du récipient en verre obtenu dans l'étape de fabrication de récipient en verre à l'aide d'un liquide de nettoyage comprenant de l'eau, une solution aqueuse d'un acide, une solution aqueuse d'un tensioactif ou une solution aqueuse d'un acide à laquelle est ajouté un tensioactif, et une étape d'élimination de contrainte permettant de chauffer et d'augmenter la température du récipient en verre nettoyé dans l'étape de nettoyage et de refroidir ensuite le récipient en verre afin d'éliminer toute contrainte de celui-ci, la température du