摘要：
The present invention relates to a nonwoven fabric having increased strength by controlling stereoregularity and a manufacturing method thereof. The nonwoven fabric with improved strength according to the present invention is prepared with a base weight of 13 gsm by mixing 5 to 10 parts by weight of a low-crystalline polypropylene with 90 to 95 parts by weight of a polypropylene resin, and adjusting a stereoregularity index to 91 to 98 mol% and melting, kneading, and spinning the mixture at a spinning speed of 2,500 to 3,500 m/min. The nonwoven fabric of the present invention can easily increase strength by reducing a weight and maintain spinning stability by using only polypropylene so as not to cause a specific physical property deterioration of the nonwoven fabric, mixing with low crystalline polypropylene having a constant stereoregularity, and optimizing the speed of spinning. Accordingly, the objective of the present invention can be achieved.COPYRIGHT KIPO 2017본 발명은 입체규칙성의 조절을 통한 강도 향상 부직포 및 그 제조방법에 대한 것으로, 상기한 본 발명의 입체규칙성의 조절을 통한 강도 향상 부직포는 저결정성 폴리프로필렌 5 내지 10중량부와 폴리프로필렌 수지 90 내지 95중량부를 혼합하여 입체규칙성 지수 91 내지 98몰%로 조정하고 용융 혼련하여 방사속도 2,500 내지 3,500m/min으로 방사한 후 기초 중량 13gsm으로 제조된 것임을 특징으로 한다.상기와 같이 구성되는 본 발명의 입체규칙성의 조절을 통한 강도 향상 부직포 및 그 제조방법은 부직포의 특정한 물리적인 물성 저하를 수반하지 않도록 폴리프로필렌만을 사용하여 저중량화 하면서도, 일정한 입체규칙성을 갖는 저결정성 폴리프로필렌을 혼합하여 사용하면서 방사속도를 최적화하여 용이하게 강도 향상을 할 수 있게 하고, 또한 방사 안정성을 유지하면서 상기한 본 발명의 목적을 달성하게 하였다.