PROBLEM TO BE SOLVED: To provide a black pearlescent pigment free from the defects of a conventional platy or flaky iron oxide pigment and to provide use thereof.SOLUTION: Iron oxyhydroxide is dispersed in water or an alkaline aqueous solution containing e.g., sodium hydroxide, potassium hydroxide, or sodium aluminate, and the aqueous dispersion is hydrothermally treated at 150-300°C in a pressure vessel to obtain a scaly iron oxide particles having hematite structure, which is then heated at 350-600°C in a reducing atmosphere. Thus, scaly magnetite-structure iron oxide particles having an average length of 5-30 &mum in the direction of the plate surface and having an average length of 0.05-0.5 &mum in the thickness direction can be formed.COPYRIGHT: (C)2010,JPO&INPIT【課題】従来の板状あるいは鱗片状の酸化鉄顔料の欠点を有さない黒色光沢顔料およびその用途を提供する。【解決手段】オキシ水酸化鉄を水あるいは水酸化ナトリウム、水酸化カリウム、アルミン酸ナトリウム等のアルカリ性水溶液に分散懸濁し、懸濁水溶液を圧力容器中150~300℃で水熱処理することにより、ヘマタイト構造を有する鱗片状酸化鉄粒子を得、還元雰囲気中350~600℃に加熱する。その板面方向の平均長さが5~30μmであり、厚さ方向の平均長さが0.05~0.5μmであって、かつマグネタイト構造を有する鱗片状酸化鉄粒子とする。【選択図】図1