It possesses the specific surface of 150m2/g - 300m2/g, it has stated the synthetic nano- size crystal characteristic calcium phosphate, concerning especially hydroxyapatite. Form of the crystal characteristic calcium phosphate of nano- size is tunic to the powder or the surface. Concerning the powder of the crystal characteristic calcium phosphate of nano- size or the production method of tunic it has stated. Until the production method forms liquid crystal phase in the aqueous solution which includes calcium, phosphorus, and the surface active agent arranges that liquid crystal phase inside ammonia atmosphere and makes the crystal of nano- size form, removes the surface active agent and making use of the solvent, collects the crystal of nano- size and obtains the powder, or ammonia dilutes the liquid crystal phase which processed with the hydrophobic solvent and makes the micro emulsion form where crystal of nano- size exists in underwater, soaks the goods where the surface was covered at oxide layer in the micro emulsion, or dipping of the goods surface to in the micro emulsion ends, the liquid crystalProcess of ammonia processing of phase is abbreviated, next the organic solvent and the surface active agent are removed from the surface and tunic is obtained.150m2/g~300m2/gの比表面積を有する、合成ナノサイズ結晶性リン酸カルシウム、特にヒドロキシアパタイトについて記載している。ナノサイズの結晶性リン酸カルシウムの形状は、粉末又は表面への被膜である。ナノサイズの結晶性リン酸カルシウムの粉末又は被膜の作製方法についても記載している。その作製方法は、カルシウム、リン、そして界面活性剤を含む水溶液中に液晶相を形成し、その液晶相をアンモニア雰囲気内に配置してナノサイズの結晶を生成させ、そして溶媒を用いて界面活性剤を除去し、ナノサイズの結晶を回収して粉末を得るか、あるいはアンモニア処理した液晶相を疎水性溶媒で希釈して水中にナノサイズの結晶が存在するマイクロエマルションを生成させ、表面が酸化物層で被覆された物品をマイクロエマルションに浸漬し、あるいはマイクロエマルション中への物品表面の浸漬が終了するまで液晶相のアンモニア処理の工程を省略し、次いで有機溶媒と界面活性剤を表面から除去して被膜を得る。