Positive electrode for lithium-ion electrochemical cells are provided that have capacity retentions of greater than about 95% after 50 charge-discharge cycles when comparing the capacity after cycle 52 with the capacity after cycle 2 when cycled between 2.5 V and 4.7 V vs. Li/Li+ at 30° C. Compositions useful in the provided positive electrodes can have the formula, Li1+x(NiaMnbCoc)1−x O2, wherein 0.05≦̸x≦̸0.10, a+b+c=1, 0.6≦̸b/a≦̸1.1, c/(a+b)<0.25, and a, b, and c are all greater than zero. The process of making these positive electrodes includes firing the compositions at 850° C. to 925° C.