Provided is a method for manufacturing a suture using a biodegradable resin and a suture produced thereby. The method for preparing a suture using biodegradable resin comprises preparing a raw material comprising a polycaprolactone-paradioxanone block copolymer, introducing the prepared raw material into a hopper connected to the top of the die head, and inserting the die head at 175 ° C. Maintained at a temperature range of 200 to 200 ° C and a pressure of 85 to 115 bar, and rotating the discharge screw inside the die head in the range of 11 rpm to 13.5 rpm to melt the injected raw material through a nozzle connected to the bottom of the die head Extruding, cooling by immersing the spinning material extruded through the nozzle unit in cooling water at 16 ° C to 18 ° C, aging the cooled spinning material on 7 to 11 rollers for a period of 15 minutes to 25 minutes The step of, stretching the aged spinning material, contracting and stabilizing the drawn spinning material, and stabilizing the spinning material Including the right step to take.생분해성 수지를 이용한 봉합사 제조방법 및 이에 의해 제조된 봉합사를 제공한다. 생분해성 수지를 이용한 봉합사 제조방법은 폴리카프로락톤-파라디옥사논 블록공중합체를 포함하는 원료를 준비하는 단계, 다이헤드의 상단에 연결된 호퍼에 준비된 상기 원료를 투입하는 단계, 상기 다이헤드를 175℃ 내지 200℃의 온도 범위 및 85 bar 내지 115 bar의 압력으로 유지하고, 상기 다이헤드 내부의 방류 스크류를 11rpm 내지 13.5rpm의 범위로 회전하면서 투입된 상기 원료를 용융하여 상기 다이헤드 하단에 연결된 노즐부를 통해 압출하는 단계, 상기 노즐부를 통해 압출된 방사물을 16℃ 내지 18℃의 냉각수에 침지하여 냉각하는 단계, 냉각된 상기 방사물을 15분 내지 25분의 시간동안 7개 내지 11개의 롤러에 감아 에이징하는 단계, 에이징된 상기 방사물을 연신하는 단계, 연신한 상기 방사물을 수축하여 안정화하는 단계, 및 안정화된 상기 방사물을 권취하는 단계를 포함한다.