Disclosed is a stannous sulfide nanometer photo-thermal agent, comprising stannous sulfide quantum dots. The preparation method therefor comprises: grinding a stannous sulfide block for 20-60 minutes, and then dispersing same in an organic solvent to obtain a dispersion； sonicating the dispersion in a water bath at 5ºC-10ºC for 8-12 hours so as to obtain a sonicated dispersion； and centrifuging the sonicated dispersion, and then collecting a precipitate and drying same to obtain stannous sulfide quantum dots. The stannous sulfide nanometer photo-thermal agent has a distinct photo-thermal effect, a high chemical stability and a low toxicity； the raw materials thereof are abundant, the price thereof is cheap, and the preparation method therefor is simple； and same has a broad application prospect in the field of photo-thermal therapy. The preparation method uses raw materials which are easy to obtain, has a sample preparation process, and easily achieves large-scale production.L'invention concerne un agent photothermique nanométrique à base de sulfure stanneux, comprenant des points quantiques de sulfure stanneux. Le procédé de préparation s'y rapportant comprend : le broyage d'un bloc de sulfure stanneux pendant 20 à 60 minutes, puis la dispersion de celui-ci dans un solvant organique pour obtenir une dispersion ； l'application d'ultrasons à la dispersion dans un bain d'eau à 5 à 10°C pendant 8 à 12 heures de manière à obtenir une dispersion à laquelle des ultrasons ont été appliqués ； et la centrifugation de la dispersion à laquelle des ultrasons ont été appliqués, puis le recueil d'un précipité et le séchage de celui-ci pour obtenir des points quantiques de sulfure stanneux. L'agent photothermique nanométrique à base de sulfure stanneux a un effet photothermique marqué, une stabilité chimique élevée et une faible toxicité ； les matières premières de celui-ci sont abondantes, le prix de celui-ci est faible et le procédé de préparation de celui-ci est simple ； et il