A fibroin porous sheet which is thin and excellent in water absorption rate, water retention property, adhesion and preferably transparency upon water absorption, and a method for producing the fibroin porous sheet. Specifically, a fibroin porous sheet having a 25% compression hardness of 200 kPa to 800 kPa, a thickness of 0.25 mm to 2.5 mm, at least one surface of the sheet covering the entire surface without a nonporous film, A medical sheet using a fibroin porous sheet and a wound dressing material using the fibroin porous sheet are provided. Furthermore, a method for producing a fibroin porous sheet in which a dried fibroin porous body having a 25% compression hardness of 200 kPa to 800 kPa is compressed at a compression ratio of 7% to 40% and sliced with a band saw is provided.薄く、吸水速度、保水性、密着性及び好ましくは吸水時の透明性に優れるフィブロイン多孔質シート及びその製造方法等を提供する。詳細には、シートの少なくとも一方の表面が全面にわたり非多孔皮膜を有さない、25%圧縮硬さが200kPa~800kPaであり、厚さが0.25mm~2.5mmのフィブロイン多孔質シート、該フィブロイン多孔質シートを用いてなる医療用シート、及び該フィブロイン多孔質シートを用いてなる創傷被覆材を提供する。さらに、25%圧縮硬さが200kPa~800kPaである乾燥フィブロイン多孔質体を圧縮率7%~40%で圧縮し、バンドソーでスライスするフィブロイン多孔質シートの製造方法を提供する。