PURPOSE: A hydroxyapatite, a poly methyl methacrylate composite, and a manufacturing method thereof are provided to manufacture a composite with improved workability and physical property by using hydroxyapatite with a superior associative property with human body hard tissue.CONSTITUTION: A poly methyl methacrylate composite comprises 10-40 weight% of hydroxyapatite compound powder and 90-60 weight% of poly methyl methacrylate polymer powder. A manufacturing method of composite comprises falling stages: a step of manufacturing compound powder by mixing polymethyl methacrylate polymer powder and inorganic material powder a step of manufacturing mortar by heat-treating the mixture a step of performing molding the mortar after filling the mold and a step oft cooling and processing the molded composite.COPYRIGHT KIPO 2012본 발명은 바이오세라믹스는 우수한 생체 안정성과 반응성으로 분말 형태의 대체 재료 사용은 하고 있으나 취성으로 인하여 구조물로의 가공성이 어려워 사용 범위가 매우 제한 적이며 고분자는 가공이 용이하고 기본적 안정을 가진 재료이나 열에 약하고 생체 반응성의 문제로 연조직의 일시적 대체물로 활용하고 있는 실정이다. 따라서, 바이오세라믹스와 바이오 폴리머를 복합체로 제조함으로서 양 소재의 장점을 충분히 가지는 하이브리드 바이오소재를 제조한다. 특히,인체에 무해한 유기소재인 폴리메틸메타크릴레이트(PMMA)를 사용하고 인체 안정성 및 인체 경조직과의 결합성이 우수한 수산화아파타이트(HAp)를 혼합하여 복합체를 제조함으로써, 가공성이 우수하고 물리적 특성을 향상시키는 공법인 것을 특징으로 하는 인체 삽입용 복합체의 제조하는 공법인 것이 장점이다.