摘要：
PROBLEM TO BE SOLVED: To provide a new method for producing materials for osteoanagenesis obtained by incorporating calcium phosphate particles into a biodegradable fiber.SOLUTION: Provided is a method for producing a biodegradable fiber in which calcium phosphate fine grains are almost uniformly dispersed into the biodegradable fiber where a lactic acid-glycolic acid copolymer resin (PLGA resin) is headed in a kneader and is softened so as to be a specified viscosity, calcium phosphate fine grains are charged while rotating the blade of the kneader so as to be mixed, the blade of the kneader is continuously rotated in the heated state so as to be kneaded, a composite body in which the fine grains of calcium phosphate are dispersed into the PLGA is produced, the solvent is dissolved with a solvent and is stirred for a prescribed time to produce a spined solution in which the calcium phosphate fine grains are dispersed in the solution with the PLGA dissolved without being flocculated, and, using the spined solution, electrospinning is performed.SELECTED DRAWING: None【課題】生分解性繊維にリン酸カルシウム粒子を含有させた骨再生用材料を製造するための新たな方法の提供。【解決手段】乳酸・グリコール酸共重合体樹脂（PLGA樹脂）をニーダー中で加熱して特定粘度になるまで軟化させ、リン酸カルシウム微粒子をニーダーの羽根を回転させながら投入することによって混合し、ニーダーの羽根を前記加熱状態で継続して回転させて混練し、リン酸カルシウムの微粒子がPLGA樹脂中に分散した複合体を作製し、該複合体を溶剤で溶かし、所定時間撹拌することによって、リン酸カルシウム微粒子がPLGA樹脂が溶解された溶液中で凝集することなく分散した紡糸溶液を作製し、該紡糸溶液を用いてエレクトロスピニングすることによって、リン酸カルシウム微粒子が生分解性繊維中に略均一に分散している生分解性繊維を製造する方法。【選択図】なし