A new composite comprises (a) 10.1-99.9% by weight of elemental Ag and (b) 0.1-89.9% by weight of ZnO, wherein the sum of (a) and (b) makes 90% or more by weight of the composite and wherein the elemental Ag has a primary particle size of 10-200 nm and/or the ZnO has a primary particle size of 0.1 to below 50 &mum and/or the composite has a particle size distribution of 0.1-50 &mum and/or a BET surface area of 10-100 m2/g. The novel composite may be obtained by the steps (i) mixing a first mixture of at least one Ag-salt with a second mixture of at least one Zn-salt thereby forming a third mixture of Ag- and Zn-salts, (ii) adding the third mixture to a mixture of a carbonate source, (iii) co-precipitating of the Ag- and Zn-carbonates formed in step (ii), (iv) washing of the Ag- and Zn-carbonates and (v) thermal decompositing of the Ag- and Zn-carbonates. The novel composites are useful to impart antimicrobial properties to surfaces, articles or bulk compositions, especially to membrane systems for gas- or water separation.新規複合材料は、(a)10.1~99.9質量%の単体銀(Ag)および(b)0.1~89.9質量%の酸化亜鉛(ZnO)を含み、(a)および(b)の合計は前記複合材料の90質量%以上を構成し、単体銀は10~200nmの一次粒径を有し、および/または酸化亜鉛は0.1~50μm未満の一次粒径を有し、および/または該複合材料は0.1~50μmの粒径分布および/または10~100m2/gのBET表面積を有する。新規複合材料は:(i)少なくとも1種の銀塩の第1混合物と少なくとも1種の亜鉛塩の第2混合物とを混合し、それにより銀塩と亜鉛塩の第3混合物を形成する工程と、(ii)前記第3混合物を炭酸源の混合物に加える工程と、(iii)工程(ii)において形成された前記炭酸銀および前記炭酸亜鉛を共沈させる工程と、(iv)前記炭酸銀および前記炭酸亜鉛を洗浄する工程と、(v)前記炭酸銀および前記炭酸亜鉛の熱分解によって入手することができる。前記新規複合材料は、表面、製品またはバルク組成物に、特別にはガスまたは水分離のための膜システムに抗菌特性を与えるために有用である。