A porous, resorbable and flexible dental surgical membrane (16) is made from chitosan having a molecular weight of at least 400,000 daltons and has a thickness of from about 100 microns to about 0.5 mm. The membrane is easily insertable over a bone graft material site to confine the bone graft material (14) while allowing access to it of blood and oxygen. The high molecular weight of the chitosan may be chosen so that the membrane will not dissolve or resorb in a human mouth for a protracted period, e.g., from about 12 to about 16 weeks. The membrane is made by dissolving medical grade chitosan in aqueous acetic acid, dispersing fine silica particles into the solution to form a slurry, depositing a film of the slurry on a support surface, evaporating liquid from the slurry sufficiently to form a coherent chitosan membrane having silica particles dispersed therein, and then dissolving the silica particles with a sodium hydroxide solution followed by a water wash to form the porous chitosan membrane.La présente invention concerne une membrane pour chirurgie dentaire (16) poreuse, résorbable et souple à base de chitosane, présentant une masse moléculaire au moins égale à 400 000 daltons et une épaisseur pouvant varier denviron 100 microns à environ 0,5 mm. Ladite membrane peut être aisément introduite sur le site dimplantation dun matériau de greffe osseuse afin de confiner ledit matériau de greffe osseuse (14) tout en laissant le sang et loxygène parvenir jusquà lui. La masse moléculaire élevée du chitosane peut être choisie de façon à ce que la membrane ne se dissolve ou ne se résorbe pas dans la bouche dun être humain avant longtemps, par exemple avant environ 12 à 16 semaines. La membrane est fabriquée par un procédé consistant à dissoudre du chitosane de qualité médicale dans de lacide acétique aqueux, à disperser de fines particules de silice dans la solution pour obtenir une suspension, à déposer un film à base de ladite suspension sur une surface de support, à