PROBLEM TO BE SOLVED: To provide a method for producing a narrow-band UVB radiation (Y, Gd, Ce, Pr)Mg borate phosphor improved in uniformity, which method forms a phosphor having higher luminous intensity, and causes almost no adhesion between baked cake and a calcinating crucible.SOLUTION: The method comprises using a mixed coprecipitated oxide combining with MgO and boric acid and calcining twice to form the borate phosphor. The mixed coprecipitated oxide is formed by dissolving sources of Y, Gd, Ce and optionally Pr in an acidic solution. By adding oxalic acid or ammonia to the solution (or adding the solution to oxalic acid or ammonia), the coprecipitate of an oxalate or a hydroxide is formed, and, by baking the obtained, the mixed coprecipitated oxide is obtained.COPYRIGHT: (C)2007,JPO&INPIT【課題】均質性が改良され、より高い光度を有する燐光体を形成し、焼成されるケーキ及び焼成るつぼ間の粘着がほとんど又は全く無い、狭帯域、UVB放射、(Y、Gd、Ce、Pr)Mgボラート燐光体の製造方法を提供する。【解決手段】本発明の方法は、MgO及びホウ酸と組み合わせた混合共沈殿酸化物を使用し、2回焼成してボラート燐光体を形成する。混合共沈殿酸化物は、Y、Gd、Ce及び任意でPr源を酸性溶液中に溶解して形成する。シュウ酸又はアンモニアを上記溶液へ添加し(又はその逆)、オキザラート又は水酸化物の共沈殿物を形成し、それを更に焼成して混合共沈殿酸化物を得る。【選択図】なし