The present invention provides a silk hydrogel composition comprising 0.01 to 30% by weight of silk fibroin powder and 0.01 to 10% by weight of urea and a method for producing a silk hydrogel mask using the same, based on the total weight of the composition. According to the present invention, the raw material solubility of the silk fibroin is increased and gelled in a short time, so that a continuous process is possible, and packaging can be performed immediately after cutting, thereby eliminating the need for an additional process, thereby increasing production safety and efficiency. In addition, the silk hydrogel composition according to the present invention can exhibit excellent strength and adhesion, and at the same time control the rate of water release, and because it is a silk material with high affinity with the human body, it can reduce the irritation, moisture content, moisturizing power, exfoliation It is effective for brightening and reducing redness, so it can be used in cosmetic masks.본 발명은 조성물 총 중량에 대하여 실크 피브로인 파우더 0.01 내지 30중량% 및 우레아 0.01 내지 10중량%을 포함하는 실크 하이드로겔 조성물 및 이를 이용한 실크 하이드로겔 마스크의 제조방법을 제공한다. 본 발명에 따르면 실크 피브로인의 원료 용해도를 높이고 단시간 내 겔화되어 연속 공정이 가능하며, 커팅 후 곧바로 포장이 가능하기 때문에 추가 공정이 필요치 않아 생산 안전성 및 효율성이 증대된다. 또한, 본 발명에 의한 실크 하이드로겔 조성물은 우수한 강도와 밀착력을 보이는 동시에 수분 방출 속도를 조절할 수 있으며, 인체와의 친화성이 높은 실크 소재이기에 자극감을 감소시킬 수 있고, 수분 함유량, 보습력, 각질 제거, 브라이트닝 및 붉은기 감소에 효과적이므로 화장품용 마스크에 사용될 수 있다.