The invention relates to a composite material for dental restoration and to a process for preparing the same. According to the invention, the material is a mono-paste one and consists of 25...35%, as mass percentage, an organic phase consisting of a polymeric matrix resulting from the polymerization, in the usual conditions, of a mixture of dimethacrylic and urethane monomers and 75...65%, by weight, an inorganic phase consisting of a silanized mixture comprising glasses based on lanthanum, colloidal silica, and, possibly, nano-filling of hydroxylapatite, zirconium hydroxylapatite, graphene oxide - zirconium dioxide. As claimed by the invention, the process consists in preparing the organic phase, where the silanized inorganic phase is dispersed, resulting in a composite as a homogenous paste having antibacterial properties and a resistance to bending of 110...133 MPa.Invenţia se referă la un material compozit pentru restaurări dentare, şi la un procedeu pentru obţinerea acestuia. Materialul conform invenţiei este de tip monopastă, fiind constituit, în procente masice, din 25...35% o fază organică constând dintr-o matrice polimerică rezultată din polimerizarea în condiţii uzuale a unui amestec de monomeri dimetacrilici şi uretanici, şi 75...65% în greutate o fază anorganică constând dintr-un amestec silanizat, format din sticle pe bază de lantan, silice coloidală, eventual, nanoumplutură de hidroxilapatită, hidroxilapatită cu zirconiu, oxid de grafenă-dioxid de zirconiu. Procedeul conform invenţiei constă în realizarea fazei organice în care se dispersează faza anorganică silanizată, rezultând un compozit sub formă de pastă omogenă, având proprietăţi antibacteriene şi o rezistenţă la încovoiere de 110...133 MPa.