The invention relates to a method for preparing an osteomimetic material from which an endosseous implant for medical or veterinary use is made, said method including the steps of: i. preparing (210) a homogeneous mixture consisting of a biocompatible thermoplastic polymer and beta-tricalcium phosphate (βTCP), ii. Subjecting said mixture to an injection or extrusion molding operation (220) on a screw machine, at an injection temperature at least equal to the fusion temperature of said polymer and at a pressure of between 70 MPa and 140 Mpa so as to convert said tricalcium phosphat into a non-stoichiometric calcium apatite 3(Ca3(PO4)2)(OH)2Ca similar to that of bone. The invention also relates to a material prepared by such a method and to an endosseous implant made of said material.L'invention concerne un procédé pour l'obtention d'un matériau pour la constitution d'un implant endo-osseux à usage médical ou vétérinaire, ostéomimétique lequel procédé comprend les étapes consistant à : i. obtenir (210) un mélange homogène consistant en un polymère thermoplastique biocompatible et du phosphate tricalcique sous la forme béta ( βTCP), ii. faire subir audit mélange une opération de moulage (220) par injection ou extrusion sur une machine a vis, a une température d'injection au moins égale à la température de fusion dudit polymère et une pression comprise entre 70 MPa et 140 MPa de sorte a transformer ledit phosphate tricalcique en une apatite de calcium 3(Ca3(PO4)2)(OH)2Ca non stœchiométrique similaire a celle de l'os. L'invention concerne également un matériau obtenu par un tel procédé et un implant endo-osseux constitué de ce matériau.