Disclosed is a bionic tooth implant, which comprises a titanium base (1), a porous titanium dioxide layer (2) permeated with polyurethane and a polyurethane layer (3) as bionic tooth peridontium. The porous titanium dioxide layer (2) permeated with polyurethane is located between the titanium base (1) and the polyurethane layer (3). The preparation method of the implant comprises: (1) the titanium base (1) is treated with acid, and then micron-sized titanium dioxide powder is deposited layer-by-layer onto the surface of the titanium base (1) using an electron beam melting technology to form a porous titanium dioxide layer (2) a polyurethane prepolymer is prepared (3) the polyurethane prepolymer is coated on the porous titanium dioxide layer, then the polyurethane prepolymer permeates into the holes of the titanium dioxide layer under vacuum conditions (4) a composite material obtained in step (3) is soaked in a solution of chain extender, and a catalyst is added for reaction, after the reaction is completed, the composite material is taken out and dried.La présente invention concerne un implant dentaire bionique, qui comprend une base en titane (1, une couche poreuse de dioxyde de titane (2) imprégnée de polyuréthane et une couche de polyuréthane (3) en tant que parodonte dentaire bionique. La couche poreuse de dioxyde de titane (2) imprégnée de polyuréthane se trouve entre la base de titane (1) et la couche de polyuréthane (3). Le procédé de préparation de limplant comprend : (1) le traitement de la base de titane (1) avec de lacide, puis le dépôt de poudre de dioxyde de titane micrométrique couche par couche sur la surface de la base de titane (1) en utilisant une technologie de fusion par faisceau délectrons pour former une couche poreuse de dioxyde de titane (2) la préparation dun prépolymère de polyuréthane (3) le revêtement du prépolymère de polyuréthane sur la couche poreuse de dioxyde de titane, puis limprégnation du prépolymère de polyuréthane dans les tr