PROBLEM TO BE SOLVED: To develop materials for implantable medical devices, such as stents.SOLUTION: A stent is formed of at least a cobalt-based alloy. The cobalt-based alloy may include: 10 to 35 wt.% of a metal member selected from the group consisting of platinum (Pt), gold (Au), iridium (Ir), osmium (Os), rhenium (Re), tungsten (W), palladium (Pd), tantalum (Ta), and combinations thereof； 16 to 21 wt.% of chromium (Cr)； 9 to 12 wt.% of molybdenum (Mo)； 0 to 25 wt.% of nickel (Ni)； and cobalt (Co) in the amount making the total amount 100%. The cobalt-based alloy may be a thin outer shell of a hollow stent. The cobalt-based alloy may be used to form at least one of an inner core and an outer shell of a core-shell structure of a stent. The cobalt-based alloy may be used to form an end of a wire for forming a stent.SELECTED DRAWING: Figure 1【課題】埋め込み可能な医療器具、例えばステントのための材料を開発する。【解決手段】ステントは、少なくともコバルト基合金で構成される。コバルト基合金は、プラチナ（Ｐｔ）、金（Ａｕ）、イリジウム（Ｉｒ）、オスミウム（Ｏｓ）、レニウム（Ｒｅ）、タングステン（Ｗ）、パラジウム（Ｐｄ）、タンタル（Ｔａ）およびその組合せからなる群から選択される１０～３５重量％金属成員；１６～２１重量％クロム（Ｃｒ）；９～１２重量％モリブデン（Ｍｏ）；０～２５重量％ニッケル（Ｎｉ）；および全量を１００とする量のコバルト（Ｃｏ）を含み得る。コバルト基合金は、中空ステントの薄い外部シェルであり得る。コバルト基合金は、ステントのコア－シェル構造の内部コアおよび外部シェルの少なくとも一方を形成するために用いられ得る。コバルト基合金は、ステントを形成するためのワイヤの一端を構成するために用いられ得る。【選択図】図１