The present invention provides a method for modifying the surface of a vulcanized rubber or a thermoplastic elastomer which can economically advantageously impart various functions such as slidability and liquid leak resistance. The present invention provides a surface modification method using a vulcanized rubber or a thermoplastic elastomer as an object to be reformed, comprising: a step 1 of forming a polymerization initiation point A on the surface of the object to be reformed Functional monomer to radical polymerization of a non-functional monomer to grow a non-functional polymer chain a step 2 of forming a polymerization initiation point B on the surface of the non-functional polymer chain, starting from the polymerization starting point B A process 3 in which a polymerizable silane compound is radically polymerized and further a perfluoroether group-containing silane compound is reacted to grow a functional polymer chain, or a silane compound is added to the surface of the non-functional polymer chain, And a step 3 of reacting a perfluoroether group-containing silane compound to grow a functional polymer chain.本発明は、摺動性、耐液漏れ性などの様々な機能性を経済的に有利に付与できる加硫ゴム又は熱可塑性エラストマーの表面改質方法を提供する。 本発明は、加硫ゴム又は熱可塑性エラストマーを改質対象物とする表面改質方法であって、前記改質対象物の表面に重合開始点Aを形成する工程1と、前記重合開始点Aを起点にして非機能性モノマーをラジカル重合させて非機能性ポリマー鎖を成長させる工程2と、前記非機能性ポリマー鎖の表面に重合開始点Bを形成し、該重合開始点Bを起点にして重合性シラン化合物をラジカル重合させ、更にパーフルオロエーテル基含有シラン化合物を反応させて機能性ポリマー鎖を成長させる工程3、又は、前記非機能性ポリマー鎖の表面にシラン化合物を付加させ、更にパーフルオロエーテル基含有シラン化合物を反応させて機能性ポリマー鎖を成長させる工程3’とを含む表面改質方法である。