PROBLEM TO BE SOLVED: To provide medical devices and a method for their fabrication.SOLUTION: A biodegradable endoprosthesis is formed from an amorphous polymer having desirable biodegradation characteristics. The strength of such an amorphous polymer is enhanced by annealing for increasing a degree of crystallinity without substantially increasing biodegradation time. The degree of crystallinity of a high amorphous polymer is 10% or less prior to modification. After modification, the degree of crystallinity is usually increased by at least 20% of the original degree of crystallinity of the amorphous material, preferably by at least 100% of the original degree of crystallinity of the amorphous material, more preferably by at least 1000% of the original degree of crystallinity of the amorphous material. Currently, the preferable polymer material has the degree of crystallinity in the range of 10% to 20% after modification as described in the specification.【課題】医療デバイスおよびそれらの製造のための方法を提供すること。【解決手段】生分解性エンドプロテーゼは、望ましい生分解特性を有する非晶質ポリマーから形成される。そのような非晶質ポリマーの強度は、生分解時間を実質的に増加させることなく、結晶化度を増加させるために焼鈍することによって強化される。高非晶質ポリマーの結晶化度は、改質前には１０％以下である。改質後、結晶化度は通常、非晶質材料の元の結晶化度の少なくとも２０％だけ、好ましくは、非晶質材料の元の結晶化度の少なくとも１００％だけ、より好ましくは、非晶質材料の元の結晶化度の少なくとも１０００％だけ増加される。現在、好ましいポリマー材料は、本明細書で記載されるように、改質後に１０％から２０％までの範囲の結晶化度を有する。【選択図】なし