Provided herein are biocompatible scaffolds and methods of preparing such bioscaffolds. The methods provide a superior high surface area, interconnected nanomacroporous bioactive glass scaffold, by combining a sol-gel process and polymer sponge replication methods. The formation of a uniformly nanoporous and interconnected macroporous bioscaffold is demonstrated using a starting material comprising a 70 mol% SiO2-30 mol% CaO glass composition as an example. The bioscaffold includes a series of open, interconnected macropores with size from 300 to 600 µm, as desired for tissue ingrowth and vascularization. At the same time, coexisting nanopores provide high-specific surface area (>150 m2/g), which is needed for enhancing the structures degradation rate. These bioscaffolds hold promise for applications in hard tissue engineering.La présente invention concerne des tuteurs biocompatibles et leurs procédés de fabrication. Lesdits procédés permettent dobtenir un tuteur en verre bioactif nanomacroporeux interconnecté de qualité présentant une grande surface active, en combinant un procédé sol-gel et des procédés de réplication impliquant une éponge polymère. La fabrication dun biotuteur macroporeux uniformément nanoporeux et interconnecté est illustrée par un exemple utilisant un matériau de départ comprenant une composition de verre constituée de 70 % en moles de SiO2 et de 30 % en moles de CaO. Le biotuteur comprend une série de macropores ouverts et interconnectés dune taille de 300 à 600 µm, comme nécessaire en vue dune pénétration et dune vascularisation tissulaires. Dans le même temps, des nanopores également présents permettent davoir une grande surface spécifique (>150 m²/g), ce qui est nécessaire pour améliorer la vitesse de dégradation de la structure. Ces biotuteurs se montrent très prometteurs dans le domaine de lingénierie des tissus durs.