The present invention provides a method for producing a biodegradable polymer, comprising: irradiating a biodegradable polymer with radiation (Step 1)； And a step of depositing hydroxyapatite (HAp) by immersing the biodegradable polymer irradiated with the radiation in the simulated body fluid (SBF) solution in the step 1 (step 2). The biodegradable polymer and the hydroxypoly Apatite <； / RTI >； The biodegradable polymer and hydroxyapatite complex of the present invention can be prepared by changing the surface of the biodegradable polymer by adjusting the dose of the biodegradable polymer such as bio-cellulose (BC), which is an environmentally friendly and biocompatible material, The steps are omitted, and are easier and more environmentally friendly. In addition, steps such as the use of a strong base can be omitted, and additional processing for biocompatibility can be omitted. Furthermore, the composite prepared by the production method of the present invention has a high deposition amount of hydroxyapatite and can be used as an excellent support for bone regeneration.본 발명은 생분해성 고분자에 방사선을 조사하는 단계(단계 1)； 및 상기 단계 1에서 방사선이 조사된 생분해성 고분자를 유사체액(simulated body fluid, SBF) 용액에 침지시켜 하이드록시아파타이트(HAp)를 침착시키는 단계(단계 2)；를 포함하는 생분해성 고분자 및 하이드록시아파타이트 복합체의 제조방법을 제공한다. 본 발명의 생분해성 고분자 및 하이드록시아파타이트 복합체의 제조방법은 친환경, 생체친화적 소재인 바이오 셀룰로오스(BC) 등의 생분해성 고분자를 방사선 조사선량 조절만으로 생분해성 고분자의 표면을 변화시켜, 강염기 사용 등의 단계가 생략되고, 보다 용이하고 친환경적인 방법이다. 또한, 강염기 사용 등의 단계가 생략되어 생체적합성에 위한 추가적인 처리가 생략될 수 있다. 나아가, 본 발명의 제조방법으로 제조된 복합체는 하이드록시아파타이트의 침착량이 높아 우수한 골 재생용 유도 지지체로 사용될 수 있다.